Structures by: Barth T. F.
Total: 18
Nickel titanium oxide
NiO3Ti
Zeitschrift fuer Kristallographie, Kristallgeometrie, Kristallphysik, Kristallchemie (-144,1977) (1934) 88, 271-280
a=5.45Å b=5.45Å c=5.45Å
α=55.13° β=55.13° γ=55.13°
Cadmium titanium oxide - low temperature modification
CdO3Ti
Zeitschrift fuer Kristallographie, Kristallgeometrie, Kristallphysik, Kristallchemie (-144,1977) (1934) 88, 271-280
a=5.82Å b=5.82Å c=5.82Å
α=53.6° β=53.6° γ=53.6°
Sodium aluminium silicate
AlNaO4Si
Zeitschrift fuer Kristallographie, Kristallgeometrie, Kristallphysik, Kristallchemie (-144,1977) (1932) 81, 1 135-141
a=7.37Å b=7.37Å c=7.37Å
α=90° β=90° γ=90°
Sodium aluminate silicate *
AlNaO4Si
Zeitschrift fuer Kristallographie, Kristallgeometrie, Kristallphysik, Kristallchemie (-144,1977) (1932) 81, 1 376-385
a=7.37(2)Å b=7.37(2)Å c=7.37(2)Å
α=90° β=90° γ=90°
Silicon oxide
O2Si
American Journal of Science, Serie 5(1,1921-1938) (1932) 23, 350-356
a=7.16Å b=7.16Å c=7.16Å
α=90° β=90° γ=90°
Sodium aluminium silicate sulfate *
Al6Na8O28SSi6
Zeitschrift fuer Kristallographie, Kristallgeometrie, Kristallphysik, Kristallchemie (-144,1977) (1932) 83, 405-414
a=9.05Å b=9.05Å c=9.05Å
α=90° β=90° γ=90°
Octasodium tecto-hexaalumohexasilicate dichloride
Al6Cl2Na8O24Si6
Zeitschrift fuer Kristallographie, Kristallgeometrie, Kristallphysik, Kristallchemie (-144,1977) (1932) 83, 405-414
a=8.89Å b=8.89Å c=8.89Å
α=90° β=90° γ=90°
Iron titanate
FeO3Ti
Zeitschrift fuer Kristallographie, Kristallgeometrie, Kristallphysik, Kristallchemie (-144,1977) (1934) 88, 265-270
a=5.52Å b=5.52Å c=5.52Å
α=54.83° β=54.83° γ=54.83°
Magnesium digallium oxide
Ga2MgO4
Zeitschrift fuer Kristallographie, Kristallgeometrie, Kristallphysik, Kristallchemie (-144,1977) (1932) 82, 325-341
a=8.26(1)Å b=8.26(1)Å c=8.26(1)Å
α=90° β=90° γ=90°
Diiron titanium oxide
Fe2O4Ti
Zeitschrift fuer Kristallographie, Kristallgeometrie, Kristallphysik, Kristallchemie (-144,1977) (1932) 82, 325-341
a=8.50(1)Å b=8.50(1)Å c=8.50(1)Å
α=90° β=90° γ=90°
Magnesium diindium oxide
In2MgO4
Zeitschrift fuer Kristallographie, Kristallgeometrie, Kristallphysik, Kristallchemie (-144,1977) (1932) 82, 325-341
a=8.81(1)Å b=8.81(1)Å c=8.81(1)Å
α=90° β=90° γ=90°
Dizinc tin(IV) oxide
O4SnZn2
Zeitschrift fuer Kristallographie, Kristallgeometrie, Kristallphysik, Kristallchemie (-144,1977) (1932) 82, 325-341
a=8.61(1)Å b=8.61(1)Å c=8.61(1)Å
α=90° β=90° γ=90°
Disodium calcium silicate
CaNa2O4Si
Zeitschrift für Kristallographie - Crystalline Materials (1932) 81, 1 370-375
a=7.48(1)Å b=7.48(1)Å c=7.48(1)Å
α=90° β=90° γ=90°
Magnesium diiron(III) oxide
Fe2MgO4
Zeitschrift fuer Kristallographie, Kristallgeometrie, Kristallphysik, Kristallchemie (-144,1977) (1932) 82, 325-341
a=8.36(1)Å b=8.36(1)Å c=8.36(1)Å
α=90° β=90° γ=90°
Dimagnesium titanium oxide
Mg2O4Ti
Zeitschrift fuer Kristallographie, Kristallgeometrie, Kristallphysik, Kristallchemie (-144,1977) (1932) 82, 325-341
a=8.41(1)Å b=8.41(1)Å c=8.41(1)Å
α=90° β=90° γ=90°
Ilmenite
FeO3Ti
Zeitschrift fur Kristallographie (1934) 88, 265-270
a=5.52Å b=5.52Å c=5.52Å
α=54.83° β=54.83° γ=54.83°
NiO3Ti
NiO3Ti
Zeitschrift fur Kristallographie (1934) 88, 271-280
a=5.45Å b=5.45Å c=5.45Å
α=55.13° β=55.13° γ=55.13°
CdO3Ti
CdO3Ti
Zeitschrift fur Kristallographie (1934) 88, 271-280
a=5.82Å b=5.82Å c=5.82Å
α=53.6° β=53.6° γ=53.6°